摘要：Geopolymer is a natural adhesive material which can be developed as a substitute for cement. The natural ingredients which want to use should contain silica and alumina. This paper uses bagasse ash as a basic material of mortar geopolymer. As an adhesive, the bagasse ash should be mixed with water and another activator alkali such as sodium hydroxide (NaOH) and sodium silicate (Na2SiO3). The NaOH)s molarity variation are 8, 10, 12, 14 and 16 M with Na2SiO3/NaOH = 1,0 sand/bagasse ash = 2,75 and activator/bagasse ash = 0,42. This research use 50 × 50 × 50 mm cube sized specimen and conduct a compressive strength test with 3, 7, 14, 21 and 28 days. The fresh mortar test result showed that the use of NaOH)s molarity variation influences the slump value and time setting. The bigger NaOH molarity variation that been used, the smaller slump value. But, the time setting is increased. While the result for density and compressive strength shown that the bigger NaOH molarity variation, the bigger density and the compressive strength. Maximum compressive strength resulted from the mixture of mortar geopolymer with 16 M concentration.