摘要：Selective Laser Melting (SLM) is one of the powder based additive manufacturing technologies and it is, as well, the most rapidly growing technique in Rapid Prototyping. In this paper is presented a microstructure analysis using Scanning Electron Microscope (LEO 1525 SEM), of Ti6Al4V parts exposed into a corrosion environment. The corrosion environment was generated using a salt chamber with 5% and 10% NaCl concentration and an ACS-Sunrise climatic chamber. The parts were also subjected to tests in order to determine their micro-hardness, followed by a statistical processing of the obtained data. The parts, having a lattice structure, were built on a Selective Laser Melting machine.