摘要：This study presents curing temperature influences to behaviors of geopolymer concrete. The concrete was fly ash based, with the ratio of fly ash to alkaline activator was 65%:35%. Ratio coarse aggregate to fine aggregate was 60%:40%, ratios Na2SiO3/NaOH were 1.5:2 and 2.5. A polycarboxilate superplasticizer with ratio was 2% to fly ash weight. Form of the test specimens were cylinder with diameter of 10 cm and 20 cm high. Steam curing conducted were at 40°C, 60°C and 80°C for 24 hours. The control specimens were treated at normal moist curing. Tests conducted were compressive strength, tensile strength, porosity and elasticity modulus. The results indicated that at the elevated temperature the compressive strength increases as well as tensile strength but decreases the closed porosity of specimens. The elasticity modulus had a similar tendency.