期刊名称：Advances in Science and Technology Research Journal
印刷版ISSN：2080-4075
电子版ISSN：2299-8624
出版年度：2017
卷号：11
期号：4
页码：215-219
DOI：10.12913/22998624/80924
语种：English
出版社：Society of Polish Mechanical Engineers and Technicians
摘要：The influence of nitrogen ion implantation on the tribological properties of Stellite 6 cobalt alloy was investigated. The tribological tests were conducted using a pin / ball on disc in the atmosphere of engine fuels. In the study, cobalt alloy was implanted with 60 keV nitrogen ions at the fluence of 1∙1016 and 5∙1016 N+/cm2. The wear trace was measured using the Form Talysurf Intra Taylor Hobson profilometer. The results demonstrate that nitrogen ion implantation affects the friction coefficient and wear. The effect of nitrogen ion implantation depends on the environment in which the tribological test is carried out, the sample temperature and the presence of friction products in the friction node.