摘要：Chitosan is a type of carbohydrate compounds produced from waste marine products, in particular the class of shrimp, crabs and clams. Chitosan is often process into edible films and utilized for food packaging also has potential as a membrane for drug delivery system. Drug loading and drug release can be controlled by improve the characteristics of the membrane by adding crosslinker. The purpose of this research is to study the effect of addition of crosslinker to the rate of loading and release of ascorbic acid in the chitosan edible film.Na2SO3was used as crosslinker. Two grams of chitosan was dissolved into 100 ml of distilled water. Acetic acid andplasticizerwere added in the solution then heated at 50°C. Na2SO3solution with mass various of Na2SO3dissolved, 01026 0.3; and 0.5 grams were added about 30 mL to make edible film. The analysis include of drug loading, drug release and tensile strength. The result showed that the loading of edible film with crosslinker 0.15 g; 0.3 g; and 0.5 g respectively were 60.98 ppm; 52.53 ppm; and 40.88 ppm, meanwhile for the release with crosslinker 0.15 g; 0.3 g; and 0.5 g respectively were 3.78 ppm; 5.72 ppm; and 5.97 ppm.
关键词：enNa2SO3drug loadingdrug releasepreventionchitosanedible film