摘要：Produced water is a wastewater generated from petroleum industry with high concentration of pollutants such as Total Dissolved Solid, Organic content, and Oil and grease. Membrane technology has been currently applied for produced water treatment due to its efficiency, compact, mild and clean process. The main problem of produced water using membrane is fouling on the membrane surface which causes on low permeate productivity. This paper is majority focused on the improvement of anti-fouling performance through several modifications to increase CA membrane hydrophilicity. The membrane was prepared by formulating the dope solution consists of 18 wt-% CA polymer, acetone, and PEG additive (3 wt-%, 5 wt-%, and 7 wt-%). The membranes are casted using NIPS method and being irradiated under UV light exposure. The SEM images show that parepared membrane has asymmetric structure consist of dense layer, intermediete layer, and finger-like support layer. The filtration test shows that PEG addition increase the membrane hydrophilicity and the permeate flux increases. UV light exposure on the membrane improves the membrane stability and hydrophilicity. The imrpovement of membrane anti-fouling performance is essential to achieve the higher productivity without lowering its pollutants rejection.