摘要：Volatile organic compounds (VOC) generated from various sources like car combustion is one of the most surrounding pollutants, which can be transferred from one form to another in the presence of sunlight. In the present work the ability of the reduction of VOC have been conducted on cementitious samples surfaces by using toluene as a pollutant gas and TiO2 as an environmentally friendly photocatalyst . Two coating methods have been used (dip and spray) with two types of aqueous solution, prepared by spreading 3g/L micro and nano TiO2 powder with deionized water. A laboratory test procedure was adopted to assess the performance of the coated specimens. The specimens were subjected to toluene gas and there efficiency in gas removal was monitored with time. Furthermore, contact angle for the coated samples was also examined to investigate the hydrophilicity of the coated substrate. The results showed that TiO2 give high activity and work as a good photocatalyst for mitigation of air pollutants, and that it could be used in different ways and concentrations to obtain better air quality and aesthetic building appearance. The observed coating efficiency in reducing the toluene was more pronounced in higher than lower gas concentrations for the micro coated samples with removal efficiency equals to 13% and 10% for dipping and spraying method, respectively. While the higher removal was about 20% for both nano dipping and nanospray methods for the inlet gas concentration 3ppm. This behavior reflects the beneficial effects of TiO2 coating procedure in highly pollutant environments, like Iraq.