摘要：Combustion characteristics of a fuel defines its performance and emission characteristics. Enhancement of combustion characteristics is feasible by improvisation of fuel properties. Fuel additives were used for varying fuel properties. The evolution of ‘nano-concept’ develops countless applications in the existing technologies. In this experiment silicon nanoparticles were synthesized by ball milling micron sized silicon particles for 45 hours. The elemental and structural characterizations for the additive material were carried out by EDS, SEM and TEM analysis. Silicon nano additive was mixed in three different weight proportions with diesel to prepare the test fuels. The fuel properties variation with the addition of nano additive were studied. Engine testing was carried out at constant 1200 rpm speed and varying load conditions. Diesel fuel added with 0.5 wt% Si nanoadditive (Si 0.5) showed maximum load carrying ability among the different test fuels. In comparison with diesel at 1200 rpm and 100% load condition, an increase in torque of 5.91% was observed and BTE was increased by 8.93% with a decrease in NOxemission by 27.3%. Variation in the performance and emission characteristics of the fuels were the results of change in heat release rate and combustion timing with the addition of nano additives which could be studied from the combustion characteristic curves.