摘要：Potassium magnesium phosphate cement (MKPC) was prepared by using magnesium oxide (MgO) and potassium dihydrogen phosphate (KH2PO4, KDP). The effects of different calcination temperature, water-cement ratio and ratio on the operation of magnesium phosphate cement were studied. The effects of different water - cement ratio and ratio on the bonding strength of potassium magnesium phosphate cement and the application of potassium phosphate and magnesium cement in concrete repair and reinforcement were determined by experiments such as bending resistance, splitting, compression and bearing capacity. The experimental results show that the calcination temperature is 1100 °C, the calcination time is 1h, the settling time of magnesium oxide is 39min, and the compressive strength of one day reaches 53MPa. The water - cement ratio with the best bonding strength is 0.2, the mass ratio is 2:1.To meet the rapid repair of the construction requirements, is expected to be applied to the actual repair works.