摘要：There are various approaches to deliver therapeutic agents to the preferred target. Polymeric nanoparticles were found to have pleasing suitability as a drug carrier. The goal of this research was to optimize the synthesis method to obtain the desirable %yield and particle properties of the new biocompatible polymer-based nanoparticles. The non-toxic polymer,N-vinyl pyrrolidone (NVP) and a widely used hydrophilic biocompatible acrylic acid (AA) monomer were used to form the drug nanocarriers. The synthesis method was optimized by changing the types of initiator (KPS or V50) and the monomers molar ratio (NVP:AA). It was found that by varying both the monomer molar ratio and the type of reaction initiator, did not have significant effect on the physicochemical characteristics of the nanocarriers. The FTIR spectra of all products exhibited the peaks of carboxylic acid, carbonyl, and tertiary amine functional group vibration. The particle size of the nanocarriers was in the range of 173.6 ± 18.4 to 201.4 ± 17.1 nm with negative surface charge. However, the yield obtained increased as the initiator was altered from KPS to V50, and when the acrylic acid molar ratio was increased from 1:1 to 1:3. In conclusion, changing the initiator and monomer molar ratio may affect the physicochemical properties of the nanocarriers and the %yield of the nanocarrier product. Further investigations are essential to obtain the favorable drug nanocarriers for drug delivery.