摘要：The effect of aging process at 845° C for 24 h and casting conditions on the microstructure andmechanical properties of Ni base superalloys were investigated. Alloys under investigation weremanufactured by investment casting under various conditions of cooling rate and superheat.These alloys were solution treated at 1120 and 1180° C followed by air cooling before agingprocess. The volume fraction of TCP phases decreases with increasing casting superheat andlowering cooling rate. The grain size of aged specimens and solution treated at 118°0 C iscoarser than ones solution treated at 1120° C. The Vf of γ’ particles in case of aged with lowsuperheat specimen is higher than that in high superheat one after solution at 1120 and 1180° C.The Vf of γ' in case of aged and solution treated at 1120° C is higher than that aged withsolution treated at 1180° C. Hardness measurements of aged alloys with low and high superheatspecimens solution treated at 1120° C are higher than that of 1180° C.