摘要：Flow behavior of Al-2.0wt.%Cu-1.0wt.%Mn aluminum alloy was investigated by hot compressive test using a Gleebe-3800 thermal simulator. The test parameters about temperature and strain rate range from 573K to 773 K and from 0.01s-1to 5s-1, respectively, and the true strain is up to 0.6. It can be seen that the peak flow stress increases with increasing the strain rate and decreases by deformation temperature. And the deformation activation energy of Al-2.0wt.%Cu-1.0wt.%Mn alloy is 183.02KJ/mol. A constitutive equation has been constructed to predict the hot deformation behavior, and correlate the peak flow stress predicted with strain rate and deformation temperature.