期刊名称：Beni-Suef University Journal of Basic and Applied Sciences
印刷版ISSN：2314-8535
电子版ISSN：2314-8543
出版年度：2015
卷号：4
期号：3
页码：207-213
DOI：10.1016/j.bjbas.2015.05.013
语种：English
出版社：Elsevier
摘要：AbstractThe Egyptian magmatic ilmenite is classified as a medium-grade ore. The present work is an attempt to produce a high-quality TiO2that can be used in several industries from this medium-grade raw material using the mechanical activation, carbothermic reduction, hydrochloric acid leaching and calcination. A mixture from the ilmenite (FeTiO3) and activated carbon was milled for 30 h. This mixture was annealed at 1200 °C for one hour and the product was leached by hydrochloric acid and calcined at 600 °C for two hours. The role of the ball milling was to grind the raw ilmenite to obtain the nano size, and the carbothermic reduction was to reduce all the Fe-Ti phases to a mixture from Fe metal and TiO2. Leaching procedure was carried out to remove all the Fe metal and obtain a high-grade TiO2. After leaching and calcination of the milled and annealed mixture of FeTiO3/C under the optimal conditions, TiO2nanoparticles with a size of 10–100 nm and purity more than 95% were obtained. The qualifications of the synthesized high purity rutile nanoparticles from the Egyptian natural ilmenite match the conditions of many industrial applications.