摘要：It is well known that fretting fatigue strength is much lower than the fatigue strength of smooth specimens and the fatigue limit disappears. Many studies on fretting fatigue have been reported but most of the studies have not cover fatigue properties in the very high cycle regime more than 107cycles. In this study, an accelerated fretting fatigue testing method was developed by using an ultrasonic torsional fatigue testing machine with a clamping fretting pad. Fretting fatigue tests of CrMo steel were conducted by using the developed method. Test results showed that fretting fatigue failure occurs in the very high cycle region.