摘要：To avoid detection from Radio Detection and Ranging (Radar), one of the efforts is to use Radar absorbing material. One of the Radar wave absorbing materials is Perovskite CoTiO 3 . This Paper investigated the ability of CoTi (1-x) Mn (x) O 3 to absorb the Radar wave. CoTi (1-x) Mn (x) O 3 with variations x = 0, 0.01, 0.02, and 0.03 have been successfully synthesized using the mechanical milling method. The XRD pattern shows that the sample formed was single phase CoTiO 3 . Surface morphology resulting from measurements with SEM shows homogeneous particles and an average size of 200 nm. The results of measurements with VNA at X-band frequency (8.20 GHz - 12.4 GHz) show that the absorption ability of electromagnetic waves from CoTiO 3 increases with the increase in doping from Mn 4+ . Maximum results obtained at the composition x=0.03 (CoTi 0.97 Mn 0.03 O 3 ) with a reflection loss (RL) value is -14.56 dB (%Abs is 81.3%) at a frequency of 9.96 GHz. This result proves that CoTi (1-x) Mn (x) O 3 can be used as a Radar absorbing material at X-band frequency.