摘要：Composite structures made of 2 mm-thick titanium and 10 mm-thick carbon steel are widely used in infrastructures such as long-distance gas transportation. However, cracking, which is caused by intermetallic compounds (ICs), is a dominate failure mode in welds of this structure. Thus, a common way to improve the in-service life of is reduce the number of ICs. In this paper, we employ a novel hybrid welding method to fabricate composite structures of TA
2 titanium and Q235 carbon steel. Specifically, Ti and carbon steel is welded by laser and double Cold Metal Transfer (CMT) welding, respectively. The microstructure near the interface of Ti and steel is then examined using SEM, EBSD, EDS, with emphasis on the ICs in terms of chemical elements and morphologies. Results show that FeTi and Fe
2Ti are the main ICs near the interface, and responsible for the failure of the welds. The effect of welding heat input on the formation of ICs is investigated as well. Results show that ICs are smaller when the heat input is low. Under low heat input circumstance, the tensile strength of the weld can reach up to 420 MPa.