摘要：Pectin from sugar beet (<i>Beta vulgaris</i> L.) (SBP) was extracted from a sugar beet waste (SBW) registering a 4.4% (<i>w/w</i>) yield. SBP presented a weight-average molar mass of 459 kDa, galacturonic acid content of 52.2%, and a low esterification degree (30%). The macromolecular characteristics of SBP revealed a flexible and extended coil chain conformation. The main neutral sugars in SBP were galactose (20.7%), mannose (5.0%), and arabinose (3.60%) while ferulic acid (FA) content was 2.1 µg·mg<sup>−1</sup> sample. FA remained in the SBP chain mainly in RG I region even after suffering both, industrial processing and harsh weathering conditions. Consequently, SBP formed covalent gels induced by laccase. Covalent cross-linking content (dimers and trimer of FA) was 0.97 mg·g<sup>−1</sup> SBP. The 8-5′, 5-5′, and 8-<i>O</i>-4′ dimers of FA isomers proportions were 75, 17, and 8%, respectively. SBP gels at 4% (<i>w/v</i> ) registered storage (G′) and loss (G″) moduli final values of 44 and 0.66 Pa, respectively. SBP gels were soft and adhesive according to texture profile analysis. Scanning electron microscopy analysis of SBP lyophilized gels revealed an imperfect honeycomb-like structure with 4.5 ± 1.4 µm average cavities diameter.