摘要：Summary Biomimetic design and substrate-based surface modification of medical implants will help to improve the integration of tissue to its material interfaces. Surface energy, composition, roughness, and topography all influence the biological responses of the implants, such as protein adsorption and cell adhesion, proliferation and differentiation. In the current study, different surface structures of Ti implants were constructed using facile surface techniques to create various micro-, nano-, and nano/micro composite scale topography. We have fabricated three types of hierarchical structures of TiO2 coating on Ti implants, including nanotube structure, nano sponge-like structure, and nano/micro nest-like structure. The osteointegration and biomechanical performance of the coated Ti screws were evaluated by histology and removal of torque force test in vivo. We found that the nano/micro nest-like and nanotube structured surface possessed better osteointegration ability. It indicated that the alkaline hydrothermally treated Ti substrate was the best for bone-implant integration in terms of all in vitro and in vivo testing parameters. The alkaline hydrothermally treated surface displayed a hydrophilic (contact angle value 5.92 ± 1.2), higher roughness (Ra value 911.3 ± 33.8 nm), higher specific surface area (8.26 ± 1.051 m2/g), and greater apatite inductivity. The electrochemical surface modification may become a powerful approach to enhance metal implant to bone integration in orthopaedic applications.
Loading...