摘要：The purpose of this research is to investigate the acoustic properties of natural fibres and compare them with the values achieved by common insulation materials used in the construction of buildings. Three materials based on biomass were used for testing, namely cork, hemp and fibreboard. From the group of conventional materials, mineral wool, propylat and polyurethane foam were selected. For the purpose of determining the values of the sound absorption coefficient (α), the absorber specimens were tested using the impedance tube and two microphones method, according to standard ISO 10534-2. The measurement was performed for thicknesses of 20, 40, 60, 80 and 100 mm. The highest sound absorption of all materials was measured with a hemp sample at a frequency of 2000 Hz (α = 0.99) and a thickness of 20 mm. The lowest performance was achieved by cork at the same thickness and frequency of 100 Hz (α = 0.02). Among biomass materials, hemp dominated in the entire frequency range and at all thicknesses. The lowest values were for cork, from 160 to 500 Hz with a tendency to exceed the values of the fibreboard sample. Among conventional materials, mineral wool achieved the best results, while the lowest values were recorded for propylat with the occasional exception of the highest frequencies from 1600 to 2500 Hz.