  • 标题:Eucalyptus wood treatment and leaching behavior of CCB (Chromated Copper Borate): a field test in Brazilian Midwest
  • 本地全文:下载
  • 作者:Pedro Augusto Fonseca Lima ; Cassiano Pacheco da Silva ; Fernando Nunes Gouveia
  • 期刊名称:Research, Society and Development
  • 电子版ISSN:2525-3409
  • 出版年度:2021
  • 卷号:10
  • 期号:11
  • 页码:1-10
  • DOI:10.33448/rsd-v10i11.19746
  • 语种:English
  • 出版社:Grupo de Pesquisa Metodologias em Ensino e Aprendizagem em Ciências
  • 摘要:The use of Chromated Copper Borate (CCB) for wood treatment is known with several studies on a laboratory scale. However, there is a lack of field studies to analyze the effect of the CCB over time. This study aimed to evaluate the wood properties of Eucalyptus urophylla S.T. Blake x Eucalyptus grandis W. Mill ex Maiden (called E. urograndis), treated with CCB as well evaluate the leaching of chromium, copper and bore (Cr/Cu/B) in field test. The field experiment, with wood treated and untreated (no CCB application), was installed in 2016 and remained until 2018. Wood physico-mechanical properties were evaluated for each condition (treated and untreated) and at three different time: at 0, 1 and 2 years of field exposure. The elements (Cr/Cu/B) losses (leaching) were determined by the difference in the quantification of each element retained in the wood (retention), from year 0 (amount of original elements) in relation to years 1 and 2 of field exposure. The preservative treatment of E. urograndis wood with CCB was efficient to maintain its physical and mechanical properties (mass loss, basic density, rupture and elasticity modulus) during the 2 years of field exposure. The E. urograndis wood without CCB treatment showed reductions in the physical-mechanical properties, indicating their low natural durability. High leaching (close to 100%) for boron was observed. In addition, the total of CCB retention has not changed (statistically) after 2 years.
  • 关键词:Wood properties;Wood deterioration;Wood preservation.