摘要：The thickness of the CaCO3 layer formed on the surface of the CaMgO protective layer during a high-temperature process in air was reduced by optimizing the concentration of MgO in the CaMgO protective layer. The discharge voltage of the panel with Ca0.3Mg0.7O protective layer stabilized at low values (Vf=163V, Vs min=112V) within 40hours of aging. This duration was remarkably short for a high-γ protective layer under the air annealing process. These voltages were considerably lower those of MgO (Vf=241V, Vs min=142V).