期刊名称：Journal of Radiation Research and Applied Sciences
印刷版ISSN：1687-8507
出版年度：2015
卷号：8
期号：3
页码：433-438
DOI：10.1016/j.jrras.2015.03.006
出版社：Elsevier B.V.
摘要：Abstract Nanostructures, crystalline Zinc oxide powder were synthesized by mixing Zinc chloride (0.04M) and sodium hydroxide (0.08M) using chemical route method. 0.001M molar concentrations of {TEA} (Tri ethanolamine) in aqueous solution used to the growing reaction solution. The powder samples are annealed at 190 °C. The experimental results indicate a successful growth of Zinc oxide in solid form which is not observed ever before. XRD, SEM, {TEM} and {PL} were performed to characterize the morphology, growth and optical nature of the samples. The some Rod and particle like morphology of zinc oxide has been examined by transmission electron microscopy. The particle size was found to vary from 7 to 21 nm. The room temperature {PL} spectra exhibits low intensity {UV} emission peak at 407 nm and blue emission band around 484 nm.
关键词：Zinc oxide; Chemical route method; Nano particles; XRD; SEM; TEM
Loading...