标题：Electrochemical performance and carbon deposition resistance of M-BaZr0.1Ce0.7Y0.1Yb0.1O3-δ (M = Pd, Cu, Ni or NiCu) anodes for solid oxide fuel cells
摘要：Pd-, Cu-, Ni- and NiCu-BaZr0.1Ce0.7Y0.1Yb0.1O3-δ anodes, designated as M-BZCYYb, were prepared by impregnating M-containing solution into BZCYYb scaffold, and investigated in the aspects of electrocatalytic activity for the reactions of H2 and CH4 oxidation and the resistance to carbon deposition. Impregnation of Pd, Ni or NiCu significantly reduced both the ohmic (RΩ) and polarization (RP) losses of BZCYYb anode exposed to H2 or CH4, while Cu impregnation decreased only RΩ in H2 and the both in CH4. Pd-, Ni- and NiCu-BZCYYb anodes were resistant to carbon deposition in wet (3 mol. % H2O) CH4 at 750°C. Deposited carbon fibers were observed in Pd- and Ni-BZCYYb anodes exposed to dry CH4 at 750°C for 12 h, and not observed in NiCu-BZCYYb exposed to dry CH4 at 750°C for 24 h. The performance of a full cell with NiCu-BZCYYb anode, YSZ electrolyte and La0.6Sr0.4Co0.2Fe0.8O3-δ-Gd doped CeO2 (LSCF-GDC) cathode was stable at 750°C in wet CH4 for 130 h, indicating that NiCu-BZCYYb is a promising anode for direct CH4 solid oxide fuel cells (SOFCs).