摘要：Multi layer Zinc Oxide thin films with different pH were prepared by sol-gel spin coating technique. Zincacetate dihydrate (Zn (CH3COO)2 .2H2O), monoethanolamine (MEA,H2N(CH2CH2OH) and isopropanol (CH3C2H5OH,Merck) were used to prepare the coating solution and its pH was varied by adding ammonia and was spin coated onglass substrates at 2000 rpm for 30s. After each deposition the films were pre-heated at 200°C for 10 minutes. Thecoating was repeated for five times. Finally the films were post heated at 450oC in air atmosphere for 60 minutes.Thickness of the films was found by surface stylus profilometer. The structural properties were investigated by usingX-ray diffraction technique and grain size was calculated. The optical properties were investigated using UV-Visspectroscopy and PL studies and the optical band gap was calculated. The influence of pH on the structural and opticalproperties of ZnO thin films was reported.