摘要：This study investigated the effects of aluminum (Al) mass fraction on the performance of an epoxy-lacquer based coating. The conductivity increased and IR emissivity and gloss decreased with increased Al mass fraction. When the Al mass fraction was decreased from 40% to 30%, the adhesion and impact strength of epoxy-lacquer based coatings increased and were grade 1 and 50 Kgcm, respectively. When the Al mass fraction was decreased to 10%, the mechanical properties of epoxy-lacquer based coatings decreased. Potentiodynamic polarization and electrochemical impedance spectroscopy of coatings showed that epoxy-lacquer based coating with 30% Al mass fraction has the best corrosion resistance and the lowest porosity. The epoxy-lacquer based coating with the best stability was that of 30% Al mass fraction. Comparing epoxy-lacquer based coating with polyurethane based coating, the epoxy-lacquer based coating presents not only lower emissivity and gloss but also better mechanical properties and corrosion resistance.