期刊名称：Proceedings of the National Academy of Sciences
印刷版ISSN：0027-8424
电子版ISSN：1091-6490
出版年度：2018
卷号：115
期号：5
页码：847-854
DOI：10.1073/pnas.1717850115
语种：English
出版社：The National Academy of Sciences of the United States of America
摘要：Cooling disordered compositionally asymmetric diblock copolymers leads to the formation of nearly spherical particles, each containing hundreds of molecules, which crystallize upon cooling below the order–disorder transition temperature ( T ODT). Self-consistent field theory (SCFT) reveals that dispersity in the block degrees of polymerization stabilizes various Frank–Kasper phases, including the C14 and C15 Laves phases, which have been accessed experimentally in low-molar-mass poly(isoprene)- b -poly(lactide) (PI-PLA) diblock copolymers using thermal processing strategies. Heating and cooling a specimen containing 15% PLA above and below the T ODT from the body-centered cubic (BCC) or C14 states regenerates the same crystalline order established at lower temperatures. This memory effect is also demonstrated with a specimen containing 20% PLA, which recrystallizes to either C15 or hexagonally ordered cylinders (HEXC) upon heating and cooling. The process-path–dependent formation of crystalline order shapes the number of particles per unit volume, n / V , which is retained in the highly structured disordered liquid as revealed by small-angle X-ray scattering (SAXS) experiments. We hypothesize that symmetry breaking during crystallization is governed by the particle number density imprinted in the liquid during ordering at lower temperature, and this metastable liquid is kinetically constrained from equilibrating due to prohibitively large free energy barriers for micelle fusion and fission. Ordering at fixed n / V is enabled by facile chain exchange, which redistributes mass as required to meet the multiple particle sizes and packing associated with specific low-symmetry Frank–Kasper phases. This discovery exposes universal concepts related to order and disorder in self-assembled soft materials.