摘要：Concentrating solar thermal (CST) technologies are a feasible and promising option to tackle worldwide energy problems. These solar facilities are sometimes located near industrial sites, where their main components—including concentrating solar reflectors—are prone to significant degradation caused by corrosive agents, especially in the presence of sulfurous atmospheres such as H 2 S and SO 2 . This paper focuses on analyzing the influence of sulfurous atmospheres on the durability of reflector materials used in CST technologies. To this end, accelerated aging tests were performed on the most commonly used materials found in solar reflectors (i.e., thick silvered glass and aluminum-based reflectors) by applying the same concentrations of H 2 S and SO 2 under the same conditions of temperature and relative humidity. The results showed that the solar reflectors based on a silver reflective layer are significantly corroded by H 2 S atmospheres—several corrosion defects were found in the samples tested. However, those based on aluminum were barely affected by sulfurous environments in the conditions tested. Nonetheless, the study suggests that both reflector types are suitable candidates, depending on the purpose of the CST technology in question and the specific environmental conditions.
关键词：renewable energy; concentrating solar thermal technology; solar reflector; durability; corrosive sulfurous atmosphere; industrial environment