期刊名称：IOP Conference Series: Earth and Environmental Science
印刷版ISSN：1755-1307
电子版ISSN：1755-1315
出版年度：2019
卷号：233
期号：2
页码：022002
DOI：10.1088/1755-1315/233/2/022002
出版社：IOP Publishing
摘要：Fe was introduced into TiC-2Mo2C-8Ni-20WC-8Co cermets materials. Content of Co and Fe were 8-X and X respectively, and X was 0%, 2%, 4%, 6%, 8%. Density, bending strength and impact toughness of the material were tested. Results showed that it was feasible to add Fe into the material as binder to partially replace Co. Comparing with the specimen containing 0%Fe, properties of the specimen containing 6%Co and 2%Fe had not slashed. Its density, bending strength and impact toughness were 6.783g/cm3, 847.7MPa and 16.1J/cm2 respectively.