摘要：Linepipe steels complexly consisted of low-temperature transformation microstructures of bainitic ferrite, granular bainite, and acicular ferrite (AF) as well as polygonal ferrite (PF) which individually affect the Bauschinger effect occurring during the pipe-forming. In this study, microscopic analyses of electron back-scattered diffraction (EBSD) coupled with tension-compression and interrupted bending tests were performed for verification of the Bauschinger effect of AF and PF working as major microstructures in single-phase- and two-phase-rolled API X80 steels, respectively. With respect to microstructural effects on Bauschinger effect, the reduction in mobile dislocation density during the flattening was smaller in the AF than in the PF. However, the dislocation pile-up at low-angle substructures and high-angle grain boundaries was more frequently observed, thereby leading to the higher back stress and Bauschinger effect in the AF. Boundary kernel average misorientation (KAM) profile played a critical role in determining the Bauschinger effect because they were closely related with the back stress. Thus, the Bauschinger effect was higher in the single-phase-rolled steel than in the two-phase-rolled steel. The present ex-situ interrupted bending methods coupled with EBSD analyses are outstanding ones for the detailed explanation of Bauschinger effect and provide an important idea for the yield strength designs of linepipe steels.