摘要：, which is further crystallized as the polycrystalline ZnO inner core. The highly dispersible NS-CNTs could be incorporated in the poly[(vinylidenefluoride-co-trifluoroethylene] [P(VDF-TrFE)] copolymer, one of widely studied ferro- and piezo-electric polymer, up to the value of 15 wt% as nanofillers. The relative dielectric constant (K) of polymer nanocomposite, at 1 kHz, was greatly enhanced from 12.7 to the value of 62.5 at 11 wt% of NS-CNTs, corresponding to a 492% increase compared to that of pristine P(VDF-TrFE) with only a small dielectric loss tangent (D) of 0.1.