摘要：Popularity of conducting polymers are become widely known and researches for practical application also has been done. In order to developed a continuous process for industrial scale, we have proposed a spray pyrolysis method to synthesis a flexible conductive film of Poly(3,4-ethylenedioxythiophene) poly(styrene sulfonate) (PEDOT:PSS) on poly(ethylene terephthalate) (PET) and annealed at different temperatures and spray distances. The optimum condition that resulting a best morphology was anneal at 90 o C and 20 cm distance with electrical conductivity 4.5 S/cm. It was found that annealing at temperature higher than 90 o C will resulting a stress to a film and formed crack due to a different thermal expansion, while at the distance higher than 20 cm resulting a loss of PEDOT:PSS droplets. IR spectra shows that there is no any sign of PEDOT:PSS degradation even at 110 o C. SEM analysis also show that the thickness is well distributed and there is no any sign of crack formed Article History : Received February 24 th 2017; Received in revised form May 16 th 2018; Accepted May 20th 2018; Available online How to Cite This Article : Tarmidzi, F.M. and Sasongko, S.B. (2018) Synthesis A Flexible Conductive Film of Poly 3,4-Ethylenedioxythiophene Polystyrene Sulfonate (PEDOT:PSS) Using Spray Pyrolysis Method.
其他关键词：PEDOT:PSS;PET;Conductive polymer;Spray pyrolysis;flexible film