摘要：Controlled micro/mesopores interconnected structures of three-dimensional (3D) carbon with high specific surface areas (SSA) are successfully prepared by carbonization and activation of biomass (raw rice brans) through KOH. The highest SSA of 2475 m2 g−1 with optimized pore volume of 1.21 cm3 g−1 (40% for mesopores) is achieved for KOH/RBC = 4 mass ratio, than others. The as-prepared 3D porous carbon-based electrode materials for supercapacitors exhibit high specific capacitance specifically at large current densities of 10 A g−1 and 100 A g−1 i.e. , 265 F g−1 and 182 F g−1 in 6 M KOH electrolyte, respectively. Moreover, a high power density ca. 1223 W kg−1 (550 W L−1) and energy density 70 W h kg−1 (32 W h L−1) are achieved on the base of active material loading (~10 mg cm2) in the ionic liquid. The findings can open a new avenue to use abundant agricultural by-products as ideal materials with promising applications in high-performance energy-storage devices.