摘要：Eu(3+),Tb(3+) doped and undoped NiO films were deposited on TiO2 by a sol-gel spin-coating method as the photoanodes of dye sensitized solar cells (DSSCs). A comparative study with different structures including TiO2, TiO2/NiO and TiO2/NiO:Eu(3+),Tb(3+) as the photoanodes was carried out to illustrate the photovoltaic performance of solar cells. NiO could enhance the performance of DSSCs ascribed to acting as a barrier for the charge recombination from the fluorine doped tin oxide (FTO) to electrolyte and forming a p-n junction (NiO/TiO2). Moreover, Eu(3+), Tb(3+) co-doped NiO could accelerate the electron transfer at TiO2/dye/electrolyte interface, which further benefited the performance of solar cells. The solar cells assembled with the photoelectrodes consisting of NiO:Eu(3+),Tb(3+) and TiO2 exhibited short-circuit current density (JSC) of 17.4 mA cm(-2), open-circuit voltage (VOC) of 780 mV and conversion efficiency of 8.8%, which were higher than that with TiO2/NiO and pure TiO2. The mechanisms of the influence of NiO and NiO:Eu(3+),Tb(3+) on the photovoltaic performance of DSSCs were discussed.