摘要：We report non-Cu critical current densities of 4 . 09 ⋅ 109 A/m2 at 12 T and 2.27 ⋅ 109 A/m2 at 15 T obtained from transport measurements on a Ti-alloyed RRP Nb3Sn wire after irradiation to a fast neutron fluence of 8.9 ⋅ 1021 m−2. These values are to our knowledge unprecedented in multifilamentary Nb3Sn, and they correspond to a J c enhancement of approximately 60% relative to the unirradiated state. Our magnetometry data obtained on short wire samples irradiated to fast neutron fluences of up to 2.5 ⋅ 1022 m−2 indicate the possibility of an even better performance, whereas earlier irradiation studies on bronze-processed Nb3Sn wires with a Sn content further from stoichiometry attested a decline of the critical current density at such high fluences. We show that radiation induced point-pinning centers rather than an increase of the upper critical field are responsible for this J c enhancement, and argue that these results call for further research on pinning landscape engineering.