摘要:Copper sheath is the first choice for manufacturing high- T c superconducting wires and tapes because of its high electrical and thermal conductivities, low-cost and good mechanical properties. However, Cu can easily react with superconducting cores, such as BSCCO, MgB2 and pnictides, and therefore drastically decrease the transport J c. Here, we report the fabrication of Cu-sheathed Sr1−xKxFe2As2 tapes with superior J c performance using a simple hot pressing method that is capable of eliminating the lengthy high-temperature sintering. We obtained high-quality Sr1−xKxFe2As2 tapes with processing at 800 oC for 30 minutes and measured high T c and sharp transition. By this rapid fabrication, Cu sheath does not give rise to apparent reaction layer, and only slightly diffuses into Sr-122 core. As a consequence, we achieved high transport J c of 3.1 × 104 A/cm2 in 10 T and 2.7 × 104 A/cm2 in 14 T at 4.2 K. The in-field J c performance is by far the highest reported for Cu-sheathed high- T c conductors. More importantly, Cu-sheathed Sr-122 tapes also showed a high J e value of 1.0 × 104 A/cm2 in 10 T at 4.2 K, which has reached the widely accepted practical level for applications. These results demonstrate that Cu is a very promising sheath for the practical application of pnictide conductors.