摘要：Nanoporous anatase TiO2 films were fabricated by a screen-printing method, and CuxO quantum dots (QDs) were deposited on the TiO2 films through successive ionic layer adsorption and reaction (SILAR). The amount of CuxO QDs on the TiO2 films are controlled by changing the number of SILAR cycles. The morphology, microstructure, optical, and photoelectrochemical properties of different CuxO sensitized TiO2 films (CuxO/TiO2) were investigated in detail. The nanoporous TiO2 film offers a large surface area for anchoring QDs. QD deposited samples exhibited a significant improvement in photoelectrochemical performance than the bare of TiO2. CuxO/TiO2, prepared with 7 SILAR cycles, showed the best photoelectrochemical properties, where the photocurrent density was enhanced to 500.01 μA/cm(2) compared with 168.88 μA/cm(2) of bare TiO2 under visible light. These results indicate that the designed CuxO/TiO2 structure possesses superior charge separation efficiency and photoelectrochemical properties.