摘要：A series of flattened-nanotube reinforced thermoplastic composites are sizably fabricated as a function of buckypaper loading. The effects of the volume fraction, nanotube alignment and length on the tensile performance of the composites are factored into a general expression. The incorporation of self-reinforcing polyphenylene resin (Parmax) into a highly aligned buckypaper frame at an optimal weight ratio boosts the tensile strength and Young's modulus of the buckypaper/Parmax composite to 1145 MPa and 150 GPa, respectively, far exceeding those of Parmax and aligned buckypaper individually. The composite also exhibits improved thermal (>65 W/m-K) and electrical (~700 S/cm) conductivities, as well as high thermoelectric power (22 μV/K) at room temperature. Meanwhile, the composite displays a heterogeneously complex structure. The hexyl groups of Parmax noncovalently interact with the honeycomb structure of the flattened nanotube through π-stacking and CH-π interaction, correspondingly improving the dispersity of polymer on the nanotube surface and the interfacial stress transferring while the high alignment degrees of nanotube facilitate phonon and charge transport in the composites.