摘要：In this paper, NaOH solution was used to treat straw fiber modified alkali slag cement, which enhanced the interfacial bonding between straw fiber and cementitious materials. The results showed that the best modification effect of straw fibers was obtained by soaking 3% NaOH solution for 16 hours. The compressive strength and flexural strength of alkali slag cement specimens cured for 28 days are 81.5 MPa and 10.9 MPa respectively. The toughness of the composites increases with the increase of fiber content. The flexural strength of straw fiber composites treated with NaOH solution and without NaOH solution increased by 5.6% and 11.3% compared with those without NaOH solution, and the compressive strength of straw fiber composites treated with NaOH solution increased by 34.08% compared with those without NaOH solution when the content of straw fiber was 10%.