其他摘要：The evolution of mechanical properties of a third-generation Al–Cu–Li alloy, AA2050, with different initial tempers (as-quenched WQ, naturally aged T34 and peak-aged T84) during creep-ageing has been investigated in this study. A set of creep-ageing tests was carried out under 150 MPa at 155 °C with different durations for all initial temper conditions and tensile tests were performed subsequently to acquire the main mechanical properties of the creep-aged alloys, including the yield strength, ultimate tensile strength and uniform elongation. The evolution of these mechanical properties during creep-ageing has been discussed in association with precipitation behaviour of AA2050 alloys with different initial tempers. The results indicate that the T34 alloy is the best choice for creep age forming (CAF) applications among these initial tempers, as it provides better yield strength and uniform elongation concurrently after creep-ageing. In addition, a work hardening rate analysis has been carried out for all the creep-aged alloys, helping to understand the detailed dislocation/precipitate interaction mechanisms during plastic deformation in the creep-aged AA2050 alloys with WQ, T34 and T84 initial tempers.
关键词：Initial temper ;mechanical property ;Al;Cu;Li alloy ;AA2050 ;creep age forming /
work hardening
其他关键词：Initial temper ; mechanical property ; Al–Cu–Li alloy ; AA2050 ; creep age forming ; work hardening