摘要：Gypsum and gypsum-cement-pozzolanic composites are of significant interest as materials and products for building decoration. The current tendency to reduce the consumption of gypsum-based materials and products in the context of growth and development of the finishing materials market depends on the decrease in their competitiveness compared to peers. This leads to significant interest in improving the quality of products based on gypsum and gypsum-cement-pozzolanic binder. Dispersed reinforcement is one of the ways of improving performance characteristics. The role of the type of reinforcing fibers in the formation of the gypsum-cement-pozzolanic composites structure and properties is studied in article. The influence relations of the cellulose fibers content with varying grinding degrees on the relative flexural and compressive strength of a gypsum-cement-pozzolanic matrix are obtained. It was found that the optimal content of cellulose fibers in the modified gypsum-cement-pozzolanic matrix is 0.5-1% by weight of the binder, the best indicators of flexural and compressive strength are achieved by grinding cellulose fibers to 30°SR. Using scanning electron microscopy, it was found that the microstructure of a disperse-reinforced gypsum-cementpozzolanic matrix is characterized by a uniform cellulose fibers distribution, the predominance of directionally frame reinforcement with a fibers linear orientation in the sheet plane. In this way the right choice of the type, crushing degree and cellulose fibers content can improve the quality and expand the application area of the produced gypsum-cementpozzolanic composites.
其他摘要：Gypsum and gypsum-cement-pozzolanic composites are of significant interest as materials and products for building decoration. The current tendency to reduce the consumption of gypsum-based materials and products in the context of growth and development of the finishing materials market depends on the decrease in their competitiveness compared to peers. This leads to significant interest in improving the quality of products based on gypsum and gypsum-cement-pozzolanic binder. Dispersed reinforcement is one of the ways of improving performance characteristics. The role of the type of reinforcing fibers in the formation of the gypsum-cement-pozzolanic composites structure and properties is studied in article. The influence relations of the cellulose fibers content with varying grinding degrees on the relative flexural and compressive strength of a gypsum-cement-pozzolanic matrix are obtained. It was found that the optimal content of cellulose fibers in the modified gypsum-cement-pozzolanic matrix is 0.5-1% by weight of the binder, the best indicators of flexural and compressive strength are achieved by grinding cellulose fibers to 30°SR. Using scanning electron microscopy, it was found that the microstructure of a disperse-reinforced gypsum-cementpozzolanic matrix is characterized by a uniform cellulose fibers distribution, the predominance of directionally frame reinforcement with a fibers linear orientation in the sheet plane. In this way the right choice of the type, crushing degree and cellulose fibers content can improve the quality and expand the application area of the produced gypsum-cementpozzolanic composites.