摘要：A novel nitrogen-containing graphitic mesoporous carbon was prepared through MnO-templated method using polyacrylonitrile (PAN) as both carbon and nitrogen sources, and MnCO 3 as both template and catalyst precursors. The effects of preparation conditions on the physicochemical properties of obtained samples were systematically investigated. The results showed that as the decrease of the weight ratios of PAN and MnO (2:1-1:4), the increase of carbonization temperature (700-900 °C) and pre-oxidation temperature (180-200 °C), the samples had higher specific surface area, mesopores volume and ratios, up to 507 m 2 /g, 0.824 cm 3 /g and 96.83%, respectively. Moreover, the prepared samples presented relatively high graphitic degree and nitrogen contents (~2.21%). The adsorption capacity for acid red 88 (AR88) was as high as 309 mg/g, which were dramatically affected by the mesoporous properties and C- and N-containing groups on the surface of prepared carbon. The rich graphic carbon and pyridine-N in mesoporous carbon generated π-π dispersion and electrostatic interaction with AR88, respectively, which jointly were responsible for the adsorption process. The results of the isotherm and kinetic studies indicated that the AR88 adsorption on mesoporous carbon could be well depicted using Langmuir model and pseudo-2 nd -order model.