摘要：Organic solid-state lasers (OSSLs) with distributed feedback (DFB) structures or distributed Bragg reflectors (DBRs) are promising for potential application in bio-sensing and hazardous materials detection. Here, the laser performances of the all-organic DFB waveguide lasers with various grating heights ranging from 0.4 to 4.7 μm were investigated. The grating structures used as the lasing cavity were fabricated using a two-photon absorption (TPA) direct laser writing (DLW) method with an SU-8 negative photoresist. The laser active layer consisted of a rhodamine 6G (R6G) laser dye and a cellulose acetate (CA) matrix. The R6G/CA solution was spin-coated onto the quartz substrate with the cavity (grating) structures to fabricate the DFB waveguide laser devices. The diffraction order of lasing ranged from m = 4 to 7. As the grating height was increased to 1.9 μm, the slope efficiency increased for all diffraction orders and the threshold decreases for each diffraction order. The dependence of the cavity (grating) length on the laser performances was investigated. The slope efficiency increased as the cavity length increased to 300 μm. The effect of the cavity (grating) position on the slope efficiency and the threshold position of the cavity (grating) was also studied. A maximum slope efficiency of 10.2% was achieved for the DFB waveguide laser device with a cavity (grating) length of 300 μm, a cavity position at 6 mm from the emission edge of the waveguide, and an aspect ratio ≈3 between the grating height of 1.74 μm and the grating width of 0.6 μm for the diffraction order m = 6 for lasing.