摘要：Significant debate has been noted in the α-ω and ω-β phase transformations of zirconium. The initial pressure of the α-to-ω transformation at room temperature has been reported to vary from 0.25 to 7.0 GPa, while the hydrostatic transformation is believed to occur at approximately 2.2 GPa. Shear stress is commonly considered as a key factor leading to the discrepancy. However, the principal mechanisms previously proposed concluded that the phase transformation pressure would be decreased in the presence of shear stress. The experimental results of the α-ω transformation in zirconium are contrary to this conclusion. In the ω-β phase diagram of zirconium, the dT/dP along the phase boundary near the α-ω-β triple-point was reported to be either positive or negative, but no theoretical explanation, especially a quantitative one, has been proposed. This article aimed to quantitatively investigate and explain the controversies reported in the α-ω and ω-β phase transformations of zirconium by applying a new nonhydrostatic thermodynamic formalism for solid medium, which has recently been proposed and is capable of quantitatively estimating the impact of shear stress on phase transformations in solids.