摘要：Ceramic coatings were prepared on the surface of AZ91D magnesium alloy by microarc oxidation technology. The effects of different voltages on morphology, phase composition and thickness of the coatings were characterized by SEM and XRD. The corrosion resistance of the coatings was measured by electrochemical workstation. Results indicated that the microarc oxidation coatings prepared in sodium silicate electrolyte exhibited porous surface and mainly comprised MgO, Mg 2 SiO 4 and a small amount of MgAl 2 O 4 . The thickness of the oxide coatings increased rapidly with the increase of voltage. The coating prepared at 400V voltage had good electrochemical corrosion resistance in 3.5wt% NaCl solution.