摘要：The composite phase change material was prepared via the impregnation method using diatomaceous as the carrier and stearic acid as the phase change material. The effects of diatomite content, temperature, immersion time and pressure on the mass ratio of stearic acid and diatomaceous earth in the composite phase change materials were discussed. The experimental results showed that the optimum conditions for preparing stearic acid/diatomite composite phase change material were immersion temperature of 80℃, socking time of 2 h, diatomite mass fraction of 23.04%, and vacuum degree of 0.03 MPa. Finally, the infrared spectroscopy analysis of stearic acid/diatomite composite phase change energy storage material showed that there is no chemical reaction between stearic acid and diatomite. And they are held together by intermolecular forces.
其他摘要：The composite phase change material was prepared via the impregnation method using diatomaceous as the carrier and stearic acid as the phase change material. The effects of diatomite content, temperature, immersion time and pressure on the mass ratio of stearic acid and diatomaceous earth in the composite phase change materials were discussed. The experimental results showed that the optimum conditions for preparing stearic acid/diatomite composite phase change material were immersion temperature of 80℃, socking time of 2 h, diatomite mass fraction of 23.04%, and vacuum degree of 0.03 MPa. Finally, the infrared spectroscopy analysis of stearic acid/diatomite composite phase change energy storage material showed that there is no chemical reaction between stearic acid and diatomite. And they are held together by intermolecular forces.