摘要：Preirradiation graft polymerization of styrene in a poly(tetrafluoroethylene) (PTFE) film was examined by time-resolved small-angle neutron scattering (SANS). A crosslinked PTFE film, thickness of which is about 50 μm, was irradiated by γ-ray and immersed in a mixed solvent of styrene monomer and toluene. SANS elucidated that graft polymerization proceeds by two reaction processes (I) and (II). In process (I) at 0<𝑡<200 min, graft polymerization occurs at an interface between crystalline and amorphous PTFE domains and the grafted polystyrene segregates from PTFE, forming a thin layer with a sharp interface. In process (II) at 200<𝑡<600 min, grafted PS layer starts to bridge between crystalline domains. At the end of process (II), 40% of total crystalline PTFE domain is covered by the grafted PS chains.