摘要：The effect of fiber contents on wear behavior of date palm leaf reinforced polyvinyl pyrrolidone (PVP/DPL) composites has been experimentally investigated. The test samples with fillers in 10, 20, 30, and 40% based on weight of fibers were prepared using injection molding. The optimum fiber content (i.e., 26 wt%) for maximum mechanical strength of the composites was determined by regression analysis. The dry sliding wear tests were conducted for each composition at different sliding velocities (0.392, 0.471, and 0.549 m/s) and sliding distances (188, 254, and 376 m) by applying normal loads of 5, 10, 15, and 20 N using pin-on-disc wear testing machine. The specific wear rate, wear loss, and coefficient of friction were plotted against the normal load and sliding distance at all sliding velocities. The results reveal that incorporation of date palm leaf fibers leads to significant improvement in the wear resistance of composites up to optimum fiber content and then decreases as fiber content increases. Further, it is found that surface modification has significant effect on wear performance. Worn surfaces of some selected samples were studied by scanning electron microscopy to analyze the wear mechanism.