出版社：Defence Scientific Information & Documentation Centre
摘要：An experimental study has been carried out to evaluate the influence of confinement ofalumina ceramic tiles through polymer restraint, on its ballistic performance. Tiles of 99.5 per centpurity alumina were subjected to ballistic impact against 7.62 mm armour piercing projectiles atvelocities of about 820 m/s. The tiles of size 75 mm x 75 mm x 7 mm were confined on both facesby effectively bonding varying numbers of layers of polymer fabrics. These were then bondedto a 10 mm thick fibre glass laminate as a backing using epoxy resin. High performance polyethyleneand aramid polymer fabrics were used in the current set of experiments for restraining the tiles.Comparative effects of confinement on energy absorption of tiles with varied number of layersof fabrics were evaluated. It was observed that by providing effective confinement to the tile,energy absorption could be doubled with increase in areal density by about 13 per cent.Photographs of the damage and the effects of restraint on improvement in energy absorptionof ceramic tiles are presented and discussed.